Wencon UW Putty is a two-component compound, that can be applied on wet surfaces or underwater. The UW Putty is excellent for filling up holes, dents, and rebuilding surfaces which, due to high humidity, have to be done in wet conditions. Wencon UW Putty is developed for applications, where bigger quantities are needed in one process.
Typical applications are corroded hulls and all underwater parts of vessels and structures, tanks, pipes, flange faces, etc. Wencon UW Putty is also suitable for filling gaps and holes underwater or on wet surfaces, before completion with Wencon UW Cream or UW Coating.
- Can be applied on wet surfaces or underwater
- Cures underwater and on wet surfaces
- Stop leaking pipes and tanks
- Long pot-life underwater
- Strong adhesion to all metal surfaces
|Key technical data|
|Max temperature||+60- +95°C (140-199°F)|
|Mixing ratio vol.||1:1|
|Potlife at 20°C||25 min.|
|Curing time||10 - 18 hours|
|Specific volume||556 cm3 / kg|
|Product number||Product name||IMPA no.||ISSA no.|
|No. 1012||Wencon UW Putty, 1 kg (2,2lb) unit||N/A||N/A|
Wencon UW Putty
Wencon UW Putty is a two-component compound to be applied on wet surfaces or under water. The UW Putty is excellent for filling up holes, dents and rebuilding of surfaces which, due to high humidity, have to be done in wet conditions. Wencon UW Putty is developed for applications, where bigger quantities are needed in one process.
After curing Wencon UW Putty shares many of the same characteristics of metals, which together with outstanding adhesion to all metallic surfaces, makes the compound highly suitable for repair of corroded and worn metal.
Wencon UW Putty is nonconductive and will therefore not cause bi-metallic corrosion. After curing Wencon UW Putty is resistant to oil, salt water, most diluted acids and a range of solvents.
Typical applications are corroded hulls and all underwater parts of vessels and structures, tanks, pipes, flange faces, etc. Wencon UW Putty is also suitable for filling gaps and holes under water or on wet surfaces, before completion with Wencon UW Cream or UW Coating.
Wencon UW Putty has to be mixed above water in the mixing ratio 1:1 by volume.
Two-component solvent free pasty consistency epoxy repair compound, for applying under water or on wet surfaces.
Before applying, the surface must be clean from loose paint, scales, under water growth, etc. A mechanical cleaning will do, but even better, if possible, hydro jetting.
Mix the product 1:1 on a mixing plate. Then continue in your hands, wearing wet protection gloves. Mix until the product has an even color without any “stripes” and press/ rub the UW Putty hard against the surface, by hand or by using a spatula.
Depending on amount mixed and the temperature. Mixed in small amounts, the pot life is approximately 25 minutes at 20°C (68°F)
Curing will take place in 10-18 hours, but only if the temperature allows it to cure. Curing requires a temperature of at least 10˚C (50˚F), but better at 17-23°C (62-73°F) or higher.
If the coating shall be exposed to chemicals, let it cure for 7 days before exposure.
REDUCED CURING TIME WITH INFRARED
This product is tested with and suitable for infrared curing. Curing with infrared radiation can reduce curing time significantly. Result can vary, depending on circumstances and equipment used.
After curing, the product can be machined, drilled and worked like metal.
Hardness Shore D: 76 (DIN 53505)
Tensile strength: 17,6 N/mm² - 5094 p.s.i. (DIN 53454)
Modulus of elasticity: 3400 N/mm² - 375,000 p.s.i. (DIN 53454)
Rcrack: 25,3 N/mm² -19,000 p.s.i. (DIN 53454)
Shear adhesion: 15,90 N/mm² - (ASTM D1002)
Adhesion to steel: 6,5 N/mm² - (ISO 4624)
556 cm3 per kilogram (33,9 cu inch/kg)
Corrosion and heavy load: 60°C (140°F)
Light load or no load: 95°C (203°F)
As filler: 95°C (203°F)
The compound is resistant to oil, water, salt water and most diluted acids and alkalis as well as a range of solvents.
At 20°C (68°F) : 3 years
Read the Wencon Instruction for Use and the Material Safety Data Sheet.