Wencon Putty is a very quick curing, two component, epoxy compound supplied in a practical stick format, which is easy to use.
This multipurpose epoxy paste is ideal for a wide range of emergency repairs where an ultra-quick curing and moldable compound is required. Typical applications are patching sealing and filling of cracks, leakages and holes in pipes, on flanges, in tanks etc.
- Cures in 10-20 minutes
- Simple apply procedure with cut and knead
- Patches and seals cracks, leakages and holes
- Strong adhesion to all metal surfaces
- Fully machinable
|Key technical data|
|Max temperature||+60- +250°C (140 - 199°F)|
|Mixing ratio vol.||-|
|Potlife at 20°C||3-6 min. mixed in small amounts|
|Curing time||10-20 min.|
|Specific volume||500 cm3 / kg|
|Product number||Product name||IMPA no.||ISSA no.|
|No. 1040||Wencon Putty 8x125g (8x0,28 lb)||812342||75.553.40|
|No. 1042||Wencon Putty 4x125g (4x0,28 lb)||812329||N/A|
Wencon Putty is a quick curing, two component, epoxy compound supplied in a practical stick format, which is easy to use.
Wencon Putty exhibits many of the characteristics of metals, which together with a good adhesion to all metallic surfaces makes the repair compound highly suitable for repair of corroded and worn metals.
Wencon Putty is non-conductive and will therefore not cause bi-metallic corrosion. After curing the compound is resistant to oil, water, saltwater and most diluted acids and a range of solvents.
Heat resistance ranges from 60° C (140°F) in corrosive and heavy load environments and up to 250° (482°F) C when applied as a filling compound.
This multipurpose epoxy paste is ideal for wide range of emergency repairs where an ultraquick curing and moldable compound is required. Typical applications are sealing, filling of cracks, leakages and holes in pipes, flanges, tanks etc.
The Base and Activator is co-extruded into a 125g stick. Cut off the required amount of repair compound, knead it until an even color is obtained and apply to the damaged area.
Two-component solvent free pasty consistency epoxy repair compound, for applying under water or on wet surfaces.
Before applying, the surface must be clean from loose paint, scales, under water growth, etc. A mechanical cleaning will do, but even better, if possible, hydro jetting.
Mix the product 1:1 on a mixing plate. Then continue in your hands, wearing wet protection gloves. Mix until the product has an even color without any “stripes” and press/ rub the UW Putty hard against the surface, by hand or by using a spatula.
Depending on amount mixed and the temperature. Mixed in small amounts, the pot life is approximately 25 minutes at 20°C (68°F)
Curing will take place in 10-18 hours, but only if the temperature allows it to cure. Curing requires a temperature of at least 10˚C (50˚F), but better at 17-23°C (62-73°F) or higher.
If the coating shall be exposed to chemicals, let it cure for 7 days before exposure.
REDUCED CURING TIME WITH INFRARED
This product is tested with and suitable for infrared curing. Curing with infrared radiation can reduce curing time significantly. Result can vary, depending on circumstances and equipment used.
After curing, the product can be machined, drilled and worked like metal.
Hardness Shore D: 76 (DIN 53505)
Tensile strength: 17,6 N/mm2 - 5094 p.s.i. (DIN 53454)
Modulus of elasticity: 3400 N/mm2 - 375,000 p.s.i. (DIN 53454)
Rcrack: 25,3 N/mm2 -19,000 p.s.i. (DIN 53454)
Shear adhesion: 15,90 N/mm2 - (ASTM D1002)
Adhesion to steel: 6,5 N/mm2 - (ISO 4624)
556 ccm per kilogram (35,6 cu inch/kg)
Corrosion and heavy load: 60°C (140°F) Light load or no load: 95°C (199°F) As filler: 95°C (199°F)
The compound is resistant to oil, water, salt- water and most diluted acids and alkalis as well as a range of solvents.
At 20°C (68°F) : 3 years
Read the Wencon Instruction for Use and the Material Safety Data Sheet.